EFFECTS OF TEMPERATURE AND POLYVINYL ALCOHOL

CONCENTRATIONS IN THE SYNTHESIS OF ZINC OXIDE NANOPARTICLES

A. BELAY*, B. BEKELE, A. R. CHANDRA REDDY

Adama Science and Technology University, Applied Physics Program, Ethiopia, Adama, P.O. Box, 1888

In this research the effects of annealing temperature and polyvinyl Alcohol (PVA) concentrations on the structural and optical properties of zinc oxide nanoparticles were investigated using a simple and cost effective, sol-gel method. The materials were characterized using X-Ray Diffraction (XRD), Fourier Transform Infrared (FT-IR), UV- Vis spectroscopy, Scanning Electron Microscopy (SEM) and Fluorescence Spectroscopy.

From XRD result the synthesized ZnO has pure phase hexagonal wurtzit structure.

Crystalline size, diffraction intensity and lattice parameters are increase with increase in calcinations temperature. Similarly, it has been also observed that there was an increment in the sizes, diffraction intensity and lattice parameters as the PVA concentrations increased. The morphology of ZnO NPs was characterized by SEM at different annealing temperatures. The FT-IR peaks appeared in the region of 400-600 cm−1 indicated the successful synthesizes of ZnO. The optical absorption of ZnO NPs measured at different annealing temperatures and PVA concentrations showed red shift as the temperature and concentrations were increased. Band-gaps energy decrease as the temperature and concentration decreases are due to the changes in the quantum confinement of NPs. The peak emission of the samples is independent of the temperature but its emission intensity depends on the temperature i.e it increased as the temperatures of the samples increased.

(Received August 20, 2018; Accepted January 14, 2019)

Keywords: ZnO NPs, sol-gel method, Crytal size, Temperatures effects and different PVA concentrations

1. Introduction

Zinc oxide nanoparticles (ZnO NPs) have unique physical and chemical properties, such as high chemical stability, high electrochemical coupling coefficient, broad range of absorption radiation and high photostability with multifunctional materials [1-2]. It has wide direct band gap energy (3.37 eV), large exciton-binding energy (60 meV) and high thermal and mechanical stability at room temperature [3]. ZnO NPs have also attributed to excellent properties such as easy synthesis, tunable band gap, controlled shape and size, low cost production and non-toxic [4]. The presence of large number of extrinsic and intrinsic defects in the ZnO structures act as emission centers. It has also able to emit light in various colors such as, violet, blue, green yellow and red [6-7]. Because of these remarkable and peculiar properties it has wide applications in the areas of energy generator and photocatalysis [8-9], medical science, cosmetics, and antibacterial [10-11].

Several methods have been reported in the literatures which individually and collectively affect the shape, sizes and optical properties of ZnO NPs. The various factors are precursor concentrations [12-13], temperature [14-15], duration [16], surfactant concentrations [17], dopant concentration [11], solvent medium [18] pH of reaction mixture [19], and source of light during synthesis. Recently polymers were also used to prepare a number of oxide NPs where the polymer skeleton eventually limits the growth to a specific shape of the lattice [20-22]. The recent XRD analysis of ZnO studied by [23], showed thermal annealing lead to an improvement in the crystallinity and associated with increase in crystal size as well as increase in both Zn-O bond length and unit cell volume. In addition, it has been observed that the ZnO NPs synthesized from

*Corresponding author: [email protected]

(2)

(Zn(NO3)2.6H2O) and Polyvinyl Alcohol (PVA) under different calcinations temperatures have an effect on particles sizes, crystallinity and morphology of NPs [24-26]. Increasing the temperature makes the intensity of the peaks to get sharpened and it increased with increasing temperature.

Primarily the peak intensity is attributed to increase of the crystallinity and crystal size. Therefore, annealing temperature is an important parameter which influences the morphology and sizes of the particles. Similarly, the effect of different ratios of PVA on the morphology of ZnO nano- powders was studied via PVA-assisted freezing drying process [27]. Increasing the number of particles in a given volume affects the rate of reaction because cramming more particles into at fixed volume increases the concentration of reactant and these by increasing frequency of the collision leading to higher reaction rate. So, increasing concentrations also increase the particle size. In this research the effects of calcinations temperatures and concentrations of PVA on morphology, structure, sizes and optical properties of ZnO NPs were investigated by sol-gel method. The method has much interest in view of simplicity, low cost, reliability, and relatively gives homogenous, high purity and high quality nanopowders. And the techniques is also easier to tune the nanoparticle size, shape and crystallinity.

2. Materials and methods

2.1. Materials

Polyvinyl Alcohol ([-CH2CHOH-]n used as chelating agent and Zinc nitrate hex-hydrate (Zn(NO3)2. 6H2O) were used as the precursor chemical and both are purchased from Himedia, India: assay> 99.2 %.

2.2. Synthesis methods

ZnO NPs were prepared by sol-gel method [28]. 6 gm of Polyvinyl Alcohol was dissolved in 60 ml of double distilled water and stirred for 30 min till a homogenous milk white solution obtained. Again 2 gm of zinc nitrate hexa-hydrate (Zn(NO3)2.6H2O) also dissolved in 20 ml of double distilled water and stirred by magnetic stirrer for 15 min. Zinc nitrate hexa-hydrate (Zn(NO3)2.6H2O) solution was added into chelating agent, Polyvinyl Alcohol (PVA) solution drop by drop at 70 0C under suitable magnetic stirring for 2 hrs. The mixture solution should be stirred till the gel like substances are formed. The gel sample was allowed to dry in an oven at 160 ℃ for 12 hrs. The sample was calcinated in muffle furnace (Model No: MC2-5/5/10-12, Biobase, Chaina) at the temperature of 400-600 0C in open air for 8 hrs. The same procedure was followed to prepare PVA concentrations dependent (1.89, 2.27, and 3.34 M) ZnO NPs at the temperature of 400 ℃.

2.3. Characterization methods

The X-ray diffraction (XRD) pattern for ZnO nanoparticles were analyzed using XPERT- PRO X-ray diffractometer by generating Cu-Kα radiation (λ=1.5418Ả). It is used to determine the crystalline phase of the synthesized nanoparticles. An X-ray generator operates at a voltage of 40 kV and applied current of 30 mA at room temperature. Intensities were measured at room temperature for angle range of

2   10

0

 2   80

. All the diffraction peaks are well indexed to the hexagonal ZnO wurtzite structure (JCPDS card no. 36-1451). The average nano crystalline size was calculated from the Debye Scherrer formula as follows [29]

cos 9 .

 0

D (1)

where

,

,

and D are x-ray wavelength, Bragg’s diffraction angle, full width at half maximum of the peak and average grain size of the crystalline particle respectively. The lattice parameters ‘a’ and ‘c’ and the spacing distance dhkl for the wurtzite structure of ZnO can be calculated using the Eq. (2) and (3)

(3)

 sin 3

 1

a

and

 sin

c (2)

4 ) 3 ( ) (

3

2

2 2 2

al

2

k hk h c d

hkl

ac

(3)

The unit cell volume (V) of the hexagonal system was calculated by using the following formula

V  0 . 866 a

3

c

(4) The Zn-O bond length (L) is given by

2 2

2

2 ) (1

3 z c

La   and z is given by

4 1 3 2

2

c

z a (5)

The morphology of the resulting nanoparticles was characterized using Scanning Electron Microscope (Hitachi, H-7600). The optical absorption of the samples was measured by UV-Vis- NIR spectrophotometer (Perkin Elmer, Lambda 950) in the wavelength regions of 200-500 nm at 2 nm resolutions. The band gap energy of ZnO NPs is calculated using Eq.(6)

Ehc

(4)

The vibrational spectra of ZnO NPs were measured by FT-IR (Perkin Elmer 65) in the range of wave number from 400-4000 cm−1. The photoluminescence properties of ZnO NPs were measured by spectrofluorometer (Fluoromax-4, Spectrofluorometer) at room temperature with Xe lamp as the excitation light source at resolution of 1 nm. The excitation and emission spectra are 264 and 380-500 nm respectively.

3. Results and discussion

3.1. X-ray diffraction

The XRD patterns of ZnO NPs synthesized by the sol-gel method at different annealing temperature of 400, 500 and 600 ℃ showed in Fig.1. All XRD diffraction peaks of ZnO powders are in a good agreement with wurzite structure (hexagonal phase, space group P63mc) with lattice parameters a=b= 3.249 A0 and c= 5.206 A0 as reported in (JCPDS card no. 36-1451). Nine characteristic peaks were appeared at 2

 31.802°, 34.468°, 36.306°, 47.600°, 56.592°, 62.951°, 66.411, 67.91 69.152° corresponding to (100), (002), (101), (102), (110), (103), (200), (112) and (201) of crystal planes. The samples (101) peak is the most intense peak that shows the plane is a preferred growth plane. The diffraction peak intensity also markedly increases with annealing temperature as shown in Fig. 1a-c. This may indicate that high annealing temperature provides sufficient energy to crystallites to orient in proper equilibrium sites and causes an increase in intensity [30-31]. The average crystal sizes of ZnO NPs were calculated by Debye Scherrer formula using Eq. (1) based on the full width at half-maximum (FWHM) of the peaks and is shown in the Table 1. The average crystal sizes of ZnO NPs at annealed temperature of 400, 500 and 600 ℃ are 22 nm, 24 nm and 29 nm respectively. This result shows that, the average crystal sizes of ZnO NPs increased as the annealing temperature increased which is in good agreement with the result reported previously by [23-26]. The thermal annealing lead to an improvement in

(4)

the crystallinity and associated with increase in crystal size, diffraction intensity as well as increase in both the Zn-O bond length and unit cell volume as shown in Table 2. On other hand, the Full- Width at Half Maxima (FWHM) of ZnO NPs decreases as the annealing temperatures increased.

30 35 40 45 50 55 60 65 70 75 80

0 4000 8000 12000 16000 20000 24000 28000

Intensity /au

Two theta /degree c

b

a

100 002

101

102 110

103

200 112

201

Fig. 1. XRD patterns of ZnO NPs synthesized at annealing temperatures of a) 400 ℃, b) 500 ℃ and c) 600 ℃ respectively.

The effects of annealing temperature on the lattice parameter of ZnO NPs were calculated using Eq. (2) and shown in Table 2. The lattice parameters are temperature dependent i.e. an increase in temperature leads to expansion of lattice parameters. The lattice parameters of pure zinc oxide reported by (JCPDS card no. 36-1451) are a= 0.325 nm and c= 0.521 nm are match with value obtained for ZnO NPs synthesized in this research. In addition, the nearly constant value of c/a ratio confirms that annealing of ZnO nanostructure does not make noticeable deformation in the lattice constant.

Table 1. Crystal size of ZnO NPS estimated using Debye –Scherer formula at the temperature of 400℃, 500℃ and 600℃.

Temperature/ 0C Particle size (D)/nm

400 22 ±3

500 24 ±3

600 29 ±6

Table 2. Lattice parameter, spacing distance, unit cell volume and bond length of synthesized ZnONPs at different annealing temperatures.

Temperatures hkl lattice parameter dhkl (nm) V(A03) L(A0) a(nm) c(nm) c a

400℃ 101 0.2857 0.4952 1.733 0.1871 35.00 1.7871

500℃ 101 0.2859 0.4955 1.733 0.1872 35.07 1.7887

600℃ 101 0.2860 0.4957 1.733 0.1873 35.11 1.7892

Fig. 2 shows XRD patterns of ZnO NPs synthesized by changing concentration of PVA solution (1.89, 2.27 and 3.34M) at 400℃ respectively. The X-ray diffraction peaks of ZnO NPs with different concentrations are 2θ = 31.99°, 34.45°, 36.32°, 47.60°, 56.86°, 62.93° and 67.86°

which correspond to reflecting from (100), (002), (101), (110),(120),(103) and (112) of crystal planes respectively. The calculated average crystal sizes of ZnO NPs are 19, 22 and 24 nm for PVA concentrations of 1.89, 2.27 and 3.34 M respectively as shown in Table 3. The particle sizes,

(5)

diffraction intensity and lattice parameters of ZnO NPs were increased as the PVA concentrations increased due to an increase in the number of molecules that required minimum energy [31].

20 30 40 50 60 70 80

Two theta/degree 1.89M

(a)

Intensity (a.u)

2.27M

(b) 3.34M(100)

(002) (101)

(102) (110)

(103) (112) 200 201 (c)

Fig. 2. XRD patterns of ZnO NPs synthesized using various PVA concentrations, a) 1.89M, b) 2.27M and c) 3.34M.

Table 3. Average crystal size of ZnO NPS at different PVA concentrations.

Concentration (M) Particle size (D)/nm

1.89 19 ±6

2.27 22 ±4

3.34 24 ±3

Table 4. Lattice parameter, spacing distance and unit cell volume of ZnO NPs at different PVA concentrations.

Concentrations hkl Lattice constant dhkl (nm) V(A3) a(nm) c (nm) c a

1.89 M 101 0.2856 0.4950 1.733 0.2212 34.96

2.27 M 101 0.2858 0.4952 1.732 0.2213 35.03

3.34M 101 0.2859 0.4955 1.733 0.2215 35.07

3.2. Scanning electron microscopy

Fig. 3 a-c shows the SEM images of the synthesized ZnO NPs using PVA as reducing agent at annealing temperatures of 400 0C and 500 0C respectively. As shown the figures morphology of the particles is uniform and has spherical shape. Also particles size and agglomeration of ZnO NPs increased as annealing temperature increased; this indicates the formation of larger particle sizes with small surface area to volume ration of NPs [30].

(6)

a) b)

Fig. 3. Scanning Electron Microscope images of ZnO NPs at a) 400℃ and b) 500℃

of annealing temperatures.

3.3. Fourier transform infrared spectroscopy

Fig. 4 shows the FTIR spectra of ZnO NPs measured in the wavenumber regions of 400- 4000 cm−1 at different annealing temperature. The broad and harp band observed around 3447 and 1597 cm-1 are the characteristics of hydroxyl (OH) group [32-33]. The small band found in the regions of 1718-1745 cm-1 are belong to C=O stretching vibration of carboxylic acid attached from PVA. The peaks observed in the regions of 2915-2940 cm-1 are belonging to C-H stretching. The intensity of the bands are significantly reduced at annealing temperature of 600 0C due to removal of functional groups and the formation of pure wurtzite structure.

400 800 1200 1600 2000 2400 2800 3200 3600 4000 45.0

52.5 60.0 67.5 50 55 60 65 700 10 20 30 40 50 60 70

Wave number(cm-1)

a) 400c0

470cm-1

3422cm-1

2915cm-1 1381cm-1

Transmittance (a.u)

b) 500c0

510cm-1

3447cm-1 1397cm-1

1406cm-1

2924CM-1 c) 600c0

562cm-1

3472cm-1

2940cm-1 1431cm-1

Fig. 4. FT-IR spectra of synthesized ZnO NPs at different annealing temperatures.

Similarly, the FT-IR spectra of measured ZnO NPs by varying the concentrations are shown in Fig. 5 below. From the graph, the broad band observed in the region of 3200-3600cm−1 is due to the presence of hydrogen bond (O⎯H) vibration. Presence of O-H group represents the presence of water molecules on the surface of ZnO nanoparticles [34-35]. Similarly, the transmission peaks observed in the region of 2800- 3200cm−1 are due to C-H stretching frequency of alkyl groups. The strong peak position observed in the range of 445-556 cm−1 was attributed to characteristics of ZnO wurtzite structure [35]. In general shifting in peaks positions were observed as the temperature and concentration of PVA samples are changed.

(7)

400 800 1200 1600 2000 2400 2800 3200 3600 4000 30

35 40 45 50 30 45 60 75 90 36 54 72 90

Wave number(cm-1)

517cm-1 1433cm-1 3410cm-1

1.89M

2920cm-1

Transmittance(a.u)

539cm-1

1441cm-1 3426cm-1

2.27M 2927cm-1 553cm-1

1448cm-1 2934cm-1 3447cm-1 3.34M

Fig. 5. FT-IR spectra of synthesized ZnO NPs at 1.89, 2.27 and 3.34M PVA concentrations.

3.4. UV-Vis spectroscopy

Fig. 6 shows UV-Vis absorption spectra of ZnO NPs at different annealing temperatures.

The absorption peak was observed at 370 nm, 377 nm and 382 nm for annealing temperatures of 400, 500 and 600 ℃ respectively. As temperature increased peak absorbance wavelength shifted to red due to decreasing in quantum confinement of the particles. The peaks are due to electronic transition from valence band to conduction band [34]. The band gap energy of ZnO NPs calculated using Eq. (6) were found to be 3.314, 3.251 and 3.176 eV for 400 500 and 600 ℃ respectively.

The band gaps energy of ZnO NPs decreased with increasing temperature due to various particle sizes.

320 400 480 560 640 720 800

0.00 0.02 0.04 0.06 0.08 0.10

a)

Absorbance (a.u.)

Wavelength (nm)

370nm

300 350 400 450 500 550 600 0.11

0.12 0.13 0.14 0.15 0.16

Absorbance (a.u.)

Wavelength(nm) 377nm 382nm

b) c)

Fig. 6. UV/vis Spectra of synthesized ZnO NPs at a) 400℃ b) 500℃ and c) 600℃.

Similarly, the absorption spectra of ZnO NPs synthesized using different PVA concentrations were shown in the Fig. 7. The peak absorption spectra of ZnO NPs were observed at 372, 377 and 380 nm for PVA concentrations (1.89, 2.27 and 3.34 M) respectively. The energy band gaps of ZnO NPs were decreased as the PVA concentrations increased. The red shift spectra of ZnO NPs as the PVA concentrations increase were in a good agreement with a literature reported by [34].

(8)

280 320 360 400 440 480 0.6

0.7 0.8 0.9 1.0

380nm

377nm

372nm

b) 2.27 M

a) 1.89 M C) 3.34 M

wavelength/nm

Fig. 7. UV-Vis Spectra of synthesized ZnO NPs at different PVA concentrations.

3.5. Emission spectral analysis

Fig. 8a-b shows the emission spectra of ZnO NPs at annealing temperatures of 400 and 500℃. Generally the emission spectra of ZnO NPs consist of two emission bands: one in the UV- region near 370-400 nm and the other broad band in the visible regions 400- 700 nm. Our samples exhibited UV emission peaks at 396 nm, broad peaks at 413 and 418 nm (violet region) and other peaks at 449, 466,480 and 490 nm (blue region) respectively. The emission in the UV region is attributed to the recombination between the electrons in the conduction band and holes in the valance band. The violet emission at 417 nm is ascribed to an electron transition from a shallow donor level of neutral Zni to the top level of valance band [36]. The blue emission centered on 450 nm is attributed to singly ionized VZn

-. A blue green emission centred at 481 nm is due to radiative transition of electron from the shallow donor level of Zni to an acceptor level of neutral Vzn. The green emission which is not recorded in our sample is attributed to radiative transition from conduction band to the edge of the acceptor level of OZn caused by oxygen antisites (OZn) [36]. The peak emission of our samples is independent of the temperature but emission intensity is temperature dependent i.e it increased as the temperatures of the samples increased.

380 400 420 440 460 480 500

200000 240000 280000 320000 360000 400000

Wavelength/nm

Emission spectra/au

50000 60000 70000 80000 90000 100000 110000 120000 130000

emission spectra/au

396 413 418

449 466

481

490 a

b

Fig. 8. Emission spectra of synthesized ZnO NPs at a) 400℃ b) 500℃.

4. Conclusions

Zinc oxide nanoparticles were synthesized via sol-gel methods at various temperatures and PVA concentrations. The prepared ZnO NPs were characterized by different spectroscopic techniques. The XRD and SEM images of ZnO NPs indicated increment in the particle size of as annealing temperature and PVA concentration increased. The reduction in the FWHM with

(9)

increasing temperature has confirmed the improved in crystallinity of the samples. The hexagonal wurtzite structure of ZnO was also confirmed from the diffraction pattern of the samples. From FTIR studies, with increasing annealing temperature, the presence of functional groups impurities was reduced as the particle size increased. The UV-Vis absorption peaks of the samples shifted towards higher wavelength (red shift) as the temperatures and PVA concentration increased. The emission spectra of ZnO NPs showed two peaks in ultra-violet and visible regions. The peak emission of the samples is independent of the temperature but its emission intensity depends on the temperature i.e it increased as the temperatures of the samples increased.

Acknowledgments

The authors would like to acknowledge Adama Science and Technology University and Ministry of Science and Technology of Ethiopia for financial support and National Institute of Technology, Physics Department, Warangal, India for allowing us to use the XRD for characterization of our samples and also Pusan National University, Department of Nanoscience and Nanotechnology, South Korea for allowing us to use SEM.

References

[1] V. Srivasta, D. Gusain, Y. Sharma, Journal of Ceramic International 39, 9803 (2003).

[2] S. Talam, S. R. Karumuri, N. Gunnam, http://dx.doi.org/10.5402/2012/372505.

[3] C. O. Chey, Discertation submitted to Linkoping Unversity no. 1629, 2015.

[4] S. Xu, Z. L. Wang, Nano Res. 4, 1013 (2011).

[5] M. Willander, O. Nur, J. R. Sadaf, M. I. Qadir, S. Zaman, A. Zainelabdin, N. Bano, I.

Hussain, Materials 3, 2643 (2010).

[6] A. Kołodziejczak-Radzimska, T. Jesionowski, Materials 7, 2833 (2014).

[7] Z. L. Wang, ACS Nan, 2, 1987 (2008).

[8] M. Chaari, A. Matoussi, Phys. B Condens. Matter. 407, 3441 (2012).

[9] A. Umar, Y. B. Hahn, American Scientific Publishers, California, USA, 2012.

[10] J. Podporska-Carroll, A. Myles, B. Quilty, D. E. Mccormack, R. Fagan, S. J. Hinder, D. D.

Dionysiou, S. C. Pillai, J. Hazard, J. Hazard Mater. 324, 39 (2017).

[11] P. Chand, A. Gaur, A. Kumar, U. K. Gaur, Appl. Surf. Sci. 356, 438 (2015).

[12] M. Jyoti, D. Vijay, S. Radha, IJSRP 3, 1 (2013).

[13] G. N. Narayanan, R. S. Ganesh, A. Karthigeyan, Thin Solid Films 598, 39 (2016).

[14] S. S. Kumar, P. Venkateswarlu, V. R. Rao, G. N. Rao, Int. Nano Lett. 3, 30 (2013).

[15] C. Pholnak, S. Chitnarong, S. Sumetha, J. H. David, Mater. Res. 17, 405 (2014).

[16] S. Kundu, Surface A 446, 199 (2014).

[17] A. Bagabas, A. Alshammari, M. F. A. Aboud, H. Kosslick, Nanoscale Res. Lett. 8, 516 (2013).

[18] R. Wahab, S. G. Ansari, Y. S. Kim, M. Song, H. S. Shin, Appl. Surf. Sci. 255, 4891 (2009).

[19] Y. L. Zhang, Y. Yang, J. H. Zhao, R. Q. Tan, P. Cui, W. J. Song, J. Sol-Gel Sci. Technol. 51, 198 (2009).

[20] A. Bera, D. Basak, ACS Appl. Mat. Interfaces 1, 2066 (2009).

[21] A. A. Othman, M. A. Osman, E. E. M. Ibrahim, M. A. Ali, Ceramics International 43, 527 (2017).

[22] R. Ashraft, A. Riaz, Z. N. Kayani, S. Naseerm, Materials Today: Proceeding 2, 5468 (2015).

[23] S. Preethi, A. Anitha, M. Arulmozhi, Indian Journal of Science and Technology 9, (2016).

[24] R. G. Singh, F. Singh, V. Kumar et al., Curr. Appl. Phys. 11, 624 (2011).

[25] B. Liu, Y. You, H. Zhang, H. Wu, J. Jin, H. Liu, RSC AdV, 6, 110349 (2016).

[26] L. L. Hench, J. West, The Sol-Gel Process Chemical Reviews 90, 33 (1990).

[27] T. K. Kundu, N. Karak, P. Barik, S. Saha, International Journal of Soft Computing and Engineering (IJSCE) 1, 19 (2011).

[28] B. D. Cullity, S. R. Stock, Elementary of X-ray Diffraction, third ed., Englewood Cliffs,

(10)

Prentice-Hall, NJ, 2001.

[29] A. Nehal, M. Salahuddin, K. Aged, M. Ebtisam, Tanta Unversity, Egypt. 5, 82 (2015).

[30] R. Davood, Journal of physical chemistry, Bu Ali Sina, Hamedan, Iran 50, 932 (2011).

[31] S. Alireza, M. Monsen, G. Mansour, Journal of luminescence 3, 78 (2009).

[32] P. Jamdagni, P. Khatri, I. S. Rana, Journal of King Saud University Science 30, 2168 (2018).

[33] M. Ahmed, E. Abd, A. Sarhan, A. Hasan, Journal Lumin. 4, 65 (2016).

[34] Y. Wang, C. Zhang, S. Bi, G. Luo, Chem. Phy. Letter 202, 130 (2010).

[35] A. K. Mishra, R. K. Srivastava, S. G. Prakash, Journal of Alloys and Compounds 539, 1 (2012).

Referințe

DOCUMENTE SIMILARE

Eucalyptus globulus leaf extract facilitates green synthesis of zinc oxide nanoparticles under ambient conditions for estimation of antibacterial, antioxidant and

ZnO NPs 10 ppm treatment significantly increased plant height, biomass, number of spikelets per spike, spike length, number of grains per spike compared to

The graphene oxide - zinc oxide nanocomposite adsorbent offers a synergy toward fluoride removal from contaminated drinking water.Thus prepared graphene oxide -

This work highlights a simplistic route for synthesizing zinc oxide nanoparticles via a direct chelating reaction achieved by adding zinc nitrate to dicarboxylic

The bis(2-hydroxy-1-naphthaldehydato)zinc(II) complex was used as a precursor to synthesize zinc oxide nanoparticles via thermal decomposition technique at different

The sensor manufactured by zinc oxide (ZnO) nanowires grown by hydrothermal technique was utilized for hydrogen gas sensing at 150 o C for about 1000 ppm concentration.. The

Zinc Oxide ZnO nanoparticles were successfully synthesized by assisting microwave radiations at different pH and time.. Precursor Zinc acetate dihydrate, propanol 2

The aim of this work is to obtain ZnO NPs from anodes of waste alkaline batteries, leach with nitric acid to obtain zinc nitrate that allows the use of